Ardesia
italiana a spacco
Application:
Exterio - Interior
Sizes:
Minimum 100 x 100 MM
Maximum 2200 x 1500 MM
Standard size:
200 x 400 - 400 x 400
300 x 300 - 250 x 500
300 x 600 - 400 x 600
500 x 500 - 600 x 600
Thickness:
Minimum 8 MM
Maximum 100 MM |
|
Chemical Analisysis:
Calcination loss: 2,6 %
Silicon: 63,8 %
Iron Oxide: 6,4 %
Aluminium Oxide: 18,7 %
Calcium Oxide: 1,0 %
Magnesium Oxide: 2,3 %
Potasium Oxide: 3,2 %
Sodium Oxide: 1,8 %
Sulphates expessed as SO3: Inf. 0,1 % |
Technical
Analysis:
Visible volumetric mass: 2736 KG/M³
Absorption coefficient: 0,40%
Breaking load through indirect stress by bending: 58 MPa
Analisi diffrattometrica quantitativa: Calcite 65%, Quarzo
10%, Dolomite 3%
Prova di attacco acido (sulfur dioxide test): 4.30
Ciclo termico: classificazione T1
Prova petrografica - Analisi minerallogica quantitatva:
carbonati: calcite 63-67%, Dolomite 1-5%
fillosilicati: minerali argillosi (illite) 25-30%
Miche detritiche <1%
Cloriti: circa 2%
Quarzo 15-20%
Pirite: <1%
Analisi granulometrica
Carbonati: granulo medio matrice 0.006 mm; granulo medio 0,02
mm
fillosilicati: minerali argillosi: <<0,001 mm
Cloriti: diametro massimo 0.08 mm x 0,03 mm; diametro minimo 0.01
x x0,006 mm
Quarzo: 0,02 mm
Pirite: diametro massimo 0,007 mm
Lunghezza media dei layer argillosi 1 mm.
Distanza media tra i piani minerali argillosi: 0,01 - 0,03 mm
|